AISI 630 SUS630 17-4pH 1.4542 pH Stainless Steel Round Bar

• Type: Stainless Steel Bars
• Standard: AISI
• Grade: 600 Series
• Certification: AISI
• Shape: Round
• Technique: Cold Rolled
• Model NO.: AISI 630 SUS630 17-4PH 1.4542 PH Stainless Steel R
• Surface Treatment: Bright
• Transport Package: Full
• Specification: Customized
• Trademark: Shanshui
• Origin: Liaocheng
• HS Code: 7201500010
• Production Capacity: 5000 Tons/Year

Product Description

Introduce

17-4PH / 630 / 1.4542 is one of the most popular and most commonly used stainless chromium-nickel alloy steels with copper additive, precipitation hardened with martensitic structure. It is characterized by high corrosion resistance while maintaining high strength properties, including hardness. Steel can operate in the temperature range from -29 ºC to 343 ºC, while retaining relatively good parameters. In addition, the materials in this grade are characterized by relatively good ductility and their corrosion resistance is comparable to 1.4301 / X5CrNi18-10.

Back to Top

Application

17-4PH, 630 and X5CrNiCuNb16-4 / 1.4542 is provided in the form of round bars, sheets, flat bars and cold-rolled strip. The material is widely used in the aerospace, marine, paper, energy, offshore and food industries for heavy-duty machine components, bushings, turbine blades, couplings, screws, drive shafts, nuts, measuring devices.

Back to Top

Chemical Component

Grade	C	Mn	P	S	Si	Cr	Ni	Cu	Cb+Ta
630 UNS S17400	0-0.07	0-1	0-0.04	0-0. 030	0-1	15-17.5	3-5	3-5	0.15-0.45

 

Smelting Option

1 EAF: Electric Arc Furnace

2 EAF+LF+VD: Refined-smelting and vacuum degassing

3 EAF+ESR: Electro Slag Remelting

4 EAF+PESR: protective atmosphere Electro Slag Remelting

5 VIM+PESR: Vacuum induction melting

 

Forming Option

1 Hot rolling process

2 Hot Forging: Electro-hydraulic; High-speed-hydraulic; Oil-hydraulic; Precision-forging

 

Heat-treatment Option

1 +A: Annealed (full/soft/spheroidizing)

2 +N: Normalized

3 +NT: Normalized and tempered

4 +QT: Quenched and tempered (water/oil)

5 +AT: Solution annealed

6 +P: Precipitation hardened

Suface Option

1 Black Surface

2 Grounded: Bright but rough ; Not precision

3 Machining for plate: Bright and precision; Little turning scar

4 Peeled/Turned: Bright and precision; Little turning scar

5 Polished: Very Bright and precision size; Not turning scar

 

Other Services

1 Cutting: Small pieces

2 CNC Machine: Produce as your drawing

3 Package: Bare/Nylon/Canvas/Wooden

4 Payment:T/T, L/C, O/A(request credit)

5 Transport:FOB/CFR/CIF/DDU/DDP (train/ship/Air)

 

Back to Top

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness
				Rockwell C (HR C)	Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Back to Top

Corrssion Resistance

The corrosion resistance of Type 17-4PH / 630 is comparable to that of Type 304 Stainless Steel in most media and superior to that of the hardenable 400 series stainless steels. Refer to NACE (National Association of Corrosion Engineers) for recommendations .

Back to Top

Heat Resistance

Grade 630 stainless steels have good resistance to oxidation. However, long-time exposure of grade 630 to temperatures of 370 to 480°C should be avoided, to prevent loss of toughness at ambient temperature. These grades should not be used at temperatures above age-hardening temperature, to avoid reduction of hardness and mechanical properties of the metal.

Back to Top

Heat Treatment

Solution treatment (Condition A) - Grade 630 stainless steels are heated at 1040°C for 0.5 h, then air-cooled to 30°C. Small sections of these grades can be oil quenched.

Hardening - Grade 630 stainless steels are age-hardened at low temperatures to achieve the required mechanical properties. During the process, superficial discoloration occurs followed by shrinkage at 0.10% for condition H1150, and 0.05% for condition H900.

Back to Top

Welding

Grade 630 stainless steels can be welded using all conventional methods, and they do not require pre-heating. Care should be taken in designing and welding of high strength steels to prevent weldment stresses.

Back to Top

Machining

Grade 630 stainless steels can be machined in their solution-treated condition. They have machining rates similar to that of grade 304 steels.