Chinese 2Cr13 steel (20Cr13) is a martensitic stainless steel with magnetic properties, good corrosion resistance and high hardness in the quenched state.
2Cr13 stainless steel is used in a wide range of applications, such as cutting tools, surgical tools, and steam turbine blades, material density is 7.75g/cm3, 2Cr13 is an old representation, the new representation is 20Cr13.
Steel Grade Designation Of 20Cr13 = 2Cr13 Stainless Steel
20 (or 2) - Average carbon content: 20/10,000 (0.2%), old designation is 2/1,000
Cr - Chromium symbol
13 - Average content of chromium: 13%
China | USA | Germany | Japan | ||||
Standard | Grade | Standard | Grade (UNS) | Standard | Grade | Standard | Grade |
GB/T 1220; | 20Cr13 | AISI, | 420 | DIN EN 10088-2; | X20Cr13 (1.4021) | JIS G4303 | SUS 420J1 |
Chemical Composition Of (20Cr13) 2Cr13 Stainless Steel
C | Si (≤) | Mn (≤) | P (≤) | S (≤) | Cr | Ni (≤) |
0.16 - 0.25 | 1 | 1 | 0.04 | 0.03 | 12.00 - 14.00 | -0.6 |
For Hot Rolled Steel Bar After Quenching and Tempering
Tensile strength: 640 N/mm2
Conditional yield strength (Non-proportional extension strength): ≥440 N/mm2
Elongation: ≥20%
Rate of reduction in area: ≥50%
Impact energy: ≥63 Aku2 (J)
Material hardness:
HBW: ≤ 223 (After annealing);
HBW: ≥ 192 (After quenching and tempering)
Notes:
Data is for steel diameter (d) less than or equal to 75mm.
1 N/mm2 = 1 MPa
Density (g/cm3): 7.75
Melting point: 1470-1510ºC
Specific heat capacity (J/Kg·K): 460 at 0-100ºC
Thermal conductivity (W/m·K):
22.2 at 100ºC
26.4 at 500ºC
Coefficients of linear thermal expansion (10-6/K):
10.3 (0-100ºC)
12.2 (0-500ºC)
Electrical Resistivity (μΩ·m): 0.55 at 20ºC
Longitudinal modulus of elasticity (kN/mm2): 200 at 20ºC
Annealing: 800-900ºC (Slow cooling)
Quenching: 920-980ºC (Cooling: Oil)
Tempering: (600-750ºC) (Rapid cooling)